[+/-] : What is a Masterbatch?

In pure form, polymers usually do not fulfil all technological requirements. Only through blending with additives is technological and economical functionality achieved. Additives are dispersed or dissolved into polymers and influence neither the constitution nor the configuration of the polymer, but their conformation.



back...

By furnishing the polymers with additives, the mechanical, electrical and chemical properties are improved, the processing is eased and the appearance of the product is changed.

The mechanical properties are changed by

* fillers
* nucleation agents
* softening agents
* foaming agents

The chemical properties are influenced by

* UV agents
* thermo stabilizers
* flame retardants

The appearance can be changed by

* pigments
* dies
* optical brighteners

The surface properties can be changed by

* antistatic agents
* slip agents
* antiblock agents

Additives can be used by themselves, as a combination of additives or as so called batches or masterbatches which contain a carrier resin.


A masterbatch, therefore, represents a concentrate of an additive or a combination of additives in a polymer.



We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Chemforecast Plastic additives supply shifts

Supply of plastic additives for the next 12-18 months looks secure and pricing spikes are beginning to ease. But buyers may have to look to new regions for continued supply.

Fred Gastrock of Townsend Polymers Services and Information in Houston forecasts global sales to hit 27 billion lbs in 2009, but the regions of supply are changing.

“Additive plants are moving toward the markets,” according to Gastrock, who points out that developing countries first build polymer plants, then resin plants and finally additive plants. However, currently there is still a strong international trade in polymer additives.

Regions and countries where additives production is growing rapidly include China with a growth rate for additives production of 8-10% by volume annually. In much of the rest of Asia and in the Middle East the annual growth rate is in the “high single digits” according to Gastrock. Production in India, Russia and Turkey is growing rapidly from a small annual production base of 10 million tons, 5 million tons, and 3.3 million tons respectively.

Philadelphia-based Rohm and Haas provides an example of the globalization occurring in the additives industry. The firm is working with Turkish firm Polisan on several projects, including a partnership for the manufacture of emulsions for the paint market. Late last year, Rohm and Haas signed a letter of intent and announced that it is in the final planning discussions with Polisan to construct a plastics additives plant in Gebze, Turkey. The plant will produce acrylic impact modifier and processing aids. Planned capacity is 40,000 metric tons annually.

Meanwhile, in China, Rohm and Haas and China’s Weihai Jinhong Polymer signed an agreement last January to form a new joint venture. Jinhong Rohm and Haas Chemicals Company Ltd. (JinHaas), intends to manufacture a complete range of quality plastics additives products and provide technical support to the building and construction and PVC packaging segments of the Chinese market according to Rohm and Hass’ Joan Hoffmeier Gorrell, business manager for building and construction, and Bill Magee, business manger for packaging, durables and transportation. The joint venture is currently awaiting Chinese government approval.

While the U.S. is not building new plants, there are few shutdowns of existing plants. For example, Rohm and Haas intends to meet slowly growing domestic market needs though its existing U.S. plants. In Europe, there have been some recent plant shutdowns. For instance, Chemtura is shutting down some antioxidant plants according to Gastrock.

Rohm and Haas, Chemtura and Ciba produce a broad range of additive types. Other sizable producers are Arkema, Rohm and Haas, Albemarle and Baerlacher. Major plasticizer producers include ExxonMobil, BASF and Eastman Chemicals according to Gastrock. He notes that large independent compounders include PolyOne, A. Schulman, Clariant and RTP.

Demand for U.S. additives is growing 3-4% by volume annually. European sales growth is slightly less, at 2-3%. Japanese sales growth is less than Europe’s. Asia sales are growing rapidly as new polymer plants come online.

Plasticizers constitute 55% of the total additives market. The various market components and their relative size (see chart).

Gastrock forecasts overall U.S. additive sales will grow 3-4% annually through 2009. The additive types increasing faster than this average are growing from a smaller base. These include light stabilizers and nucleating agents (clarifying agents). Polypropylene additive use is growing slightly faster than the average. Additives used in wood–plastic composites are also growing more rapidly than average but from a small base.

The big feedstock price surge in 2004 through early 2006 that pushed additive prices up 20-50% has slowed considerably. Margins have improved and additives producers have been able to manage most of the raw materials price increases.

Hoffmeier Gorrell and Magee “expect raw material pressures to continue to be driven by supply and demand dynamics in the feedstock industries.” Raw material prices remain extremely volatile,” they note. For example, since the fourth quarter of 2006, the cost of tin has doubled. In the first six months of 2007, Rohm and Haas announced increases on its Advastab tin-based heat stabilizers totaling 17%. An additional 10% increase went into effect on June 15.


We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Plastic additives supply shifts as prices ease

Supply of plastic additives for the next 12–18 months looks secure and pricing spikes are beginning to ease. But buyers may have to look to new regions for continued supply.

Fred Gastrock of Townsend Polymers Services and Information in Houston forecasts global sales to hit 27 billion lbs in 2009, but the regions of supply are changing. "Additive plants are moving toward the markets," according to Gastrock, who points out that developing countries first build polymer plants, then resin plants and finally additive plants. However, currently there is still a strong international trade in polymer additives.

Regions and countries where additives production is growing rapidly include China with a growth rate for additives production of 8–10% by volume annually. In much of the rest of Asia and in the Middle East the annual growth rate is in the "high single digits" according to Gastrock. Production in India, Russia and Turkey is growing rapidly from a small annual production base of 10 million tons, 5 million tons, and 3.3 million tons respectively.

Philadelphia-based Rohm and Haas provides an example of the globalization occurring in the additives industry. The firm is working with Turkish firm Polisan on several projects, including a partnership for the manufacture of emulsions for the paint market. Late last year, Rohm and Haas signed a letter of intent and announced that it is in the final planning discussions with Polisan to construct a plastics additives plant in Gebze, Turkey. The plant will produce acrylic impact modifier and processing aids. Planned capacity is 40,000 metric tons annually.

Meanwhile, in China, Rohm and Haas and China's Weihai Jinhong Polymer signed an agreement last January to form a new joint venture. Jinhong Rohm and Haas Chemicals Co. (JinHaas), intends to manufacture a complete range of quality plastics additives products and provide technical support to the building and construction and PVC packaging segments of the Chinese market according to Rohm and Haas.

While the U.S. is not building new plants, there are few shutdowns of existing plants. Rohm and Haas intends to meet slowly growing domestic market needs though its existing U.S. plants. In Europe, there have been some recent plant shutdowns. Chemtura is shutting down some antioxidant plants.

Demand for U.S. additives is growing 3–4% by volume annually. European sales growth is slightly less, at 2–3%. Japanese sales growth is less than Europe's. Asia sales are growing rapidly as new polymer plants come online. Plasticizers constitute 55% of the total additives market. The various market components and their relative size.

Rohm and Haas, Chemtura and Ciba produce a broad range of plastic additives. Other major producers include Arkema, Rohm and Haas, Albemarle and Baerlacher. Major plasticizer producers include ExxonMobil, BASF and Eastman Chemicals. Large independent compounders include PolyOne, A. Schulman, Clariant and RTP.

Gastrock forecasts overall U.S. additive sales will grow 3–4% annually through 2009. The additive types increasing faster than this average are growing from a smaller base. These include light stabilizers and nucleating agents (clarifying agents). Polypropylene additive use is growing slightly faster than the average. Additives used in wood—plastic composites are also growing more rapidly than average but from a small base.

The big feedstock price surge that took hold in 2004 through early 2006 and pushed additive prices up 20–50% has slowed considerably. Margins have improved and additives producers have been able to manage most of the raw materials price increases.



We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Antimony prices should hold at $6,000 until 2010

Antimony prices should increase to around $6,000/metric ton during the fourth quarter, and then remain elevated around that level to 2010, forecasts metals consultancy Roskill Information Services, citing a close long-term balance in supply and demand.

Importantly, recent policy reforms by China, the dominant global producer, will end decades of market instability caused by that country's tendency to dump or withdraw supply of such commodities as tungsten, tin and antimony—"which had all but destroyed mine output and development in competing countries."

Antimony prices should increase to around $6,000/metric ton during the fourth quarter, and then remain elevated around that level to 2010, forecasts metals consultancy Roskill Information Services, citing a close long-term balance in supply and demand.

Importantly, recent policy reforms by China, the dominant global producer, will end decades of market instability caused by that country's tendency to dump or withdraw supply of such commodities as tungsten, tin and antimony—"which had all but destroyed mine output and development in competing countries."

The Roskill Report, published in London, says the previous boom-or-bust market manipulation that "ravaged China's own mineral resources" has resulted this decade in widespread mine shutdowns and wide-ranging policy reforms aimed at resource conservation, orderly development, mine safety, environmental protection and value-added downstream processing, all controlled by quotas and licensing of mining, smelting and exporting. "As with everything the Chinese do in the antimony industry, the changes had worldwide effect," Roskill reports, noting that prices rose from a four-decade low of $1,000/metric ton (45¢/lb) in the world market in December 2001 to the $5,350/metric ton ($2.43/lb) level of July 2007.

"China is now also the largest importer of ores and concentrates, and its own domestic demand has also become the world's largest," the research house says, continuing that "this solid foundation for the antimony industry has reawakened interest in antimony resources in Australia, North America, Latin America, Russia and elsewhere, and new projects are under development." In fact, Australia soon will be producing over 12,000 metric tons/year of antimony metal equivalent.

Structural changes in the antimony supply sector, which began in the late 1990s, arose with growing exports from China of antimony trioxide at the expense of antimony metal. Between 1996 and 2006, Chinese exports of antimony trioxide grew from 20,000 metric tons to 41,300 metric tons. Over the same period, U.S. production fell from 25,000 metric tons to 1,500 metric tons in 2006, a 94% drop.

Installed capacity in China should be sufficient to meet world forecast trioxide demand growth of 7%/year through 2010 and idled capacity in Europe could come into play with new antimony mine output outside of China, Roskill says. However, the analysts also believe that higher-cost operations outside of China will be required to meet future global demand, pushing spot prices upward.

As for demand, flame retardants account for 70% of primary antimony demand and 90% of antimony trioxide demand. More stringent flammability standards and safety legislation, together with increased demand for plastics and information technology-related products, will result in higher demand for flame-retardants. World demand for antimony trioxide in this market is forecast to rise by 7.5% annually from an estimated 106,000 metric tons in 2004 to 152,000 metric tons by 2009.

Catalysts used to make polyethylene terephthalate (PET) plastic resins provide a further area of growth for antimony trioxide, says Roskill, especially in new industrializing countries where markets for PET containers for carbonated soft drinks, beer and mineral water are less mature. For example, Asian demand for bottle-grade PET is forecast to grow at over 10%/year to the end of this decade.

We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Flame retardant polyolefin pallets and flame retardant master batch for their production

Polyolefin-based pallets capable of passing standard pallet flammability tests are prepared by molding the pallet or one or more subassemblies thereof, of a polyolefin molding resin containing a flame retardant package containing a halogenated organic flame retardant, alumina trihydrate, and antimony trioxide. The flame retardants are advantageously supplied as a master batch at a concentration higher than that desired in the pallet or subassembly, in a polyolefin-compatible polymer.


Claims

What is claimed is:

1. A flame retardant molded polyolefin pallet comprising one or more subassemblies, at least one subassembly comprising a polyolefin containing a flame retardant package comprising as flame retardant components

a) 4-14% halogenated organic flame retardant,

b) 4-15% alumina trihydrate, and

c) 1-5% antimony trioxide, said percentages based on the weight of polyolefin and the sum of flame retardant components a) to c).

2. The pallet of claim 1 wherein the flame retardant components comprise

a) 7-12% halogenated organic flame retardant;

b) 8-12% alumina trihydrate;

c) 2-4% antimony trioxide; and

said percentages based on the weight of polyolefin and the sum of flame retardant components a) to c).

3. The pallet of claim 1, wherein subassemblies which comprise the most flammable portions of said pallet contain said flame retardant components.

4. The pallet of claim 1, wherein all of said subassemblies contain said flame retardant components.

5. The pallet of claim 1, wherein said polyolefin comprises polypropylene.

6. The pallet of claim 1, wherein said one or more subassemblies containing said fire retardant components further comprise a filler, fibrous reinforcement, or both filler and fibrous reinforcement.

7. The pallet of claim 1, further comprising one or more auxiliary flame retardants.

8. The pallet of claim 1, wherein said halogenated flame retardant comprises tetrabromobisphenol A.

9. A process for the manufacture of a flame retardant polyolefin pallet or subassembly thereof, comprising

a) supplying a polyolefin molding resin

b) supplying a flame retardant package comprising flame retardant components

b)i) from 4-14% halogenated organic flame retardant;

b)ii) from 4-15% alumina trihydrate;

b)iii) from 1-5% antimony trioxide;

c) uniformly blending said polyolefin resin with the components b)i to b)iii of said flame retardant package to form a flame retardant-containing polyolefin molding resin; and

d) molding a polyolefin pallet or subassembly thereof from said flame retardant-containing polyolefin molding resin.

10. The process of claim 9, wherein said flame retardant components are supplied in a master batch of a polyolefin compatible polymer resin containing said flame retardant components in an amount higher than the amount desired in said pallet or subassembly thereof, and supplying sufficient polyolefin to reduce the level of said flame retardant components to the range of 4-14% a), 4-15% b), and 1-5% c).

11. The process of claim 9, wherein said pallet comprises at least a top deck and a bottom deck, optionally having a plurality of columns between said top deck and said bottom deck, at least one of said top deck, said bottom deck, or said columns being molded from a polymer of different flammability characteristics than another of said top deck, bottom deck, or columns.

12. The process of claim 11, comprising molding said top deck of said flame retardant-containing polyolefin molding resin.

13. The process of claim 11, further comprising constructing said top deck or a portion thereof of a non-polyolefin polymer which exhibits greater inherent flammability resistant characteristics than polyolefin.

14. The process of claim 9, wherein said polyolefin comprises polypropylene.

15. The process of claim 9, wherein said polyolefin pallet or subassembly thereof further contains a filler, fibrous reinforcement, or a mixture thereof.

16. A flame retardant polymer master batch suitable for addition to a polyolefin molding resin to prepare the pallet or subassembly thereof of claim 1, said master batch comprising 20 weight percent or more halogenated organic flame retardant, 20 weight percent or more of alumina trihydrate; 6 weight percent or more of antimony trioxide, and at least 10 weight percent of a polymer which is compatible with polyolefin in injection molding.

17. The master batch of claim 16, comprising 20 to 25% halogenated flame retardant, 20 to 40% alumina trihydrate, 6 to 15% antimony trioxide, and minimally 10% polyolefin-compatible polymer, said percentages being based on the total weight of the master batch.

18. The master batch of claim 16, comprising 25-35% halogenated organic flame retardant, 25-40% alumina trihydrate, and 8-12% antimony trioxide, balance polyolefin.

19. The master batch of claim 16 wherein said polyolefin comprises polypropylene.

20. The master batch of claim 16, wherein said halogenated organic flame retardant comprises tetrabromobisphenol A.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention pertains to flame retardant shipping pallets of polyolefin plastic.

2. Background Art

In the past, shipping pallets were made largely of wood. More recently, numerous materials have at least partially superseded wood-based pallets. For example, pallets of injection molded polymers are being used increasingly. Such polymer pallets have numerous advantages. For example, polymer pallets are capable of being molded in complex shapes which facilitate the shipping of numerous types of articles. Polymer pallets are also easy to clean, which encourages their reuse.

Wood pallets are inherently combustible, and are rather easily ignited. While polymer articles are in general somewhat more difficult to ignite, once ignited they also constitute combustible products, and pound for pound have more potential energy than wood articles. In the shipping industry, empty pallets are often stacked together for reuse or for return to the shipper ("idle storage"). When wood pallets are so stacked and ignited, the fire is generally concentrated in an upward direction. However, when polymer pallets burn, in addition to having greater potential energy (combustibility), the flame can also spread downward by dripping. Thus, the combustion of polymer pallets involves more heat and more potential energy, a combustion mechanism not found in wood pallets. Thus, it is desirable to minimize the combustibility and heat release, and in turn lower the flame spread of polymer based pallets.

One solution which has been proposed is to produce pallets of polymers which are less flammable than pallets of commodity resins, such as polyolefins. However, such speciality polymers, e.g. polyphenylene oxide polymers, are considerably more expensive than the polyolefin polymers conventionally used to manufacture pallets. Such specialty polymers are also, in general, much more difficult to mold than polyolefins.

A standard test for pallet flammability has been established by Underwriters Laboratories, as UL 2335 "Fire Tests of Storage Pallets," referred to, for example, in WO 00/20495. In one version of this test, the "Idle Pallet Test," six stacks of pallets are assembled in a 2×3 array with a 6" longitudinal flue space longitudinally between arrays in a room with a 30 foot high flat ceiling having 165° F. (74° C.) standard response sprinklers having a design density of 0.60 gpm/ft2. An instrumented steel beam is placed near the ceiling, and the pallets are ignited by hydrocarbon soaked cellulosic bundle positioned in the flue space. The parameters assessed include flame spread, maximum steel beam temperature, and number of sprinklers activated. As can be seen, this test is a rather stringent one.

In a second version of the test, the so-called "Commodity Storage Test," a 2×2×2 array 1 of pallets 5, each carrying a Class II commodity carton 2, are placed 25 feet (7.5 m) below a 10 M watt heat release calorimeter 3 and ignited by four igniters in the center flue space, each igniter comprising a 3 inch (12.5 cm) cellulosic bundle soaked with 4 oz. (112 g) heptane in a polyethylene bag. Overhead sprinklers 4 at a height of 10 feet (3 m) are activated electromechanically when the instrumentation indicates that a sprinkler activation temperature of 286° F. (141° C.) has been reached. A series of three tests is made, with water application rates of 0.11, 0.21, and 0.31 gpm/ft2. In each test, four parameters are noted: maximum one minute mean total heat release rate; maximum one minute mean convective heat release rate; effective convective heat release rate, defined as the average convective heat release rate measured over five minutes of the most intense fire; and convective energy, the average convective heat release rate measured over the 10 minutes of most severe burning.

Although numerous flame retardants and combinations thereof are known for use in plastic articles, the stringent tests required of pallets render flame retardancy results unpredictable. Numerous flame retardants and combinations have been tested, and while many of these have been found suitable for polyolefin articles other than pallets, their use in pallets has not proven acceptable.

WO 00/20495 discloses pallets prepared from specialty resins such as polyphenylene ether resins, polycarbonate resins, vinyl aromatic graft copolymer resins, and polyetherimide resins further including arylphosphate esters and zinc chalcogenides. In U.S. Pat. No. 4,727,102, "self extinguishing" polyolefins are disclosed containing major amounts of ammonium polyphosphate, tris(2-hydroxyethyl)isocyanurate, and melamine cyanurate. However, the large amounts of additives (40%) severely compromise the properties of products prepared from the polyolefin resin.

It would be desirable to provide a polyolefin composition suitable for use in molding pallets which is injection moldable, exhibits good flame retardance in standard tests, and which is commercially cost effective. However, until now, tests of flame retardant systems for use in polyolefin polymer pallets did not result in satisfactory performance.

SUMMARY OF THE INVENTION

It has now been surprisingly discovered that polyolefin-based plastic pallets can be manufactured which satisfactorily pass standard pallet flammability tests, when the polyolefin is compounded with a fire retardant package comprising minimally a halogenated flame retardant, alumina trihydrate, and antimony trioxide. The flame retardant ingredients are preferably supplied as a master batch and incorporated into conventional polyolefin molding resins prior to injection molding.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a typical Commodity Storage Test setup to assess flammability characteristics of pallets;

FIG. 2 illustrates the average steel beam temperature in an Idle Storage Test of flame retardant polymer pallets of the subject invention and similar sized softwood pallets.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The polymer pallets of the present invention may take numerous forms. It has been found convenient to mold pallets in several subassemblies and assemble the pallets together by snap fittings, fusion or adhesive bonding, or by a variety of such assembly techniques. In this manner, non-load bearing areas may be made of thinner section, thus minimizing raw material usage. Moreover, use of a plurality of subassemblies allows pallets of more complex shape to be produced.

The polymer of which the pallets of the subject invention are constructed is polyolefin, although it is not necessary to form all parts of these polymers. Pallet portions which contribute more to ease of flammability or flame spread may be made of other polymers which are less flammable than polyolefin or which tend to melt and/or drip less than polyolefin. A pallet construction which employs portions of different flammabilities which takes advantage of these characteristics is disclosed in commonly assigned U.S. application Ser. No. 10/040,098, filed Oct. 19, 2001, incorporated herein by reference.

The polyolefin polymers may be, for example, but not by way of limitation, polyethylene, polypropylene, or polybutylene. In general, the polyolefin polymers are copolymers, for example copolymers of ethylene with propylene, 1-butene, 1-hexene, 1-octene, or mixtures thereof, or copolymers of propylene with ethylene, 1-butene, 1-hexene, 1-octene or mixtures thereof. Homo and copolymers of propylene are preferred. Different polyolefin polymers may be used for various subassemblies. Polymer blends of polyolefins with other compatible thermoplastics or with elastomeric tougheners such as elastomeric polymers of styrene, butadiene, alkyl acrylates, and the like are also useful. When such tougheners are used, they are generally present in the form of relatively small particles, or as interpenetrating polymer networks, as is well known in the art of toughened thermoplastics.

The polyolefin polymers may also be reinforced or filled. Suitable fillers include typical reinforcing and non-reinforcing fillers such as precipitated and fumed silicas, ground quartz, diatomaceous earth, ground limestone, ground dolomite, ground felspar, mica, expanded mica, precipitated calcium carbonate, etc. The term "reinforcing" with respect to fillers generally refers to fillers of small size and high surface area, for example mean particle sizes <1 µm and specific surface areas (BET) of 50 m2 /g or higher. Suitable fibrous fillers are typically short or long glass fibers. Other fibrous reinforcement such as aramid fiber, carbon fiber, boron nitride fiber, etc., may also be used, however such materials are generally more expensive than glass fibers. Some subassemblies may be filled or may contain fibrous reinforcement whereas other subassemblies may not, or may contain differing reinforcement and/or fillers. Use of continuous fiber reinforcement is also possible in some cases, particularly when polyolefin-based GMT intermediate products are used for molding, or when resin transfer molding and similar techniques are used.

The pallet or at least one of its component subassemblies must contain a flame retardant "FR" package in accordance with the subject invention. The subject invention FR package includes, in percent by weight relative to the total weight of polyolefin and FR package, from 4 to 14% halogenated organic flame retardant, preferably 7 to 12%, and more preferably 8 to 11%; from 4-15%, more preferably 8 to 12% and most preferably 9-11% alumina trihydrate; and 1-5%, more preferably 2 to 4% and most preferably about 3% antimony trioxide (Sb2 O3), these percentages being weight percents based on the weight of polymer and flame retardants. In particular, an FR package containing 8-10% halogenated organic flame retardant, 9-10% alumina trihydrate, and 3% antimony trioxide is used.

The halogenated organic flame retardant includes polyhalogenated organic compounds such as polybrominated biphenyl oxides, halogenated phosphate esters such as tris(2-chloroethyl)phosphate and the like. However, the most preferred halogenated organic flame retardants comprise tetrabromobisphenol A ("TBBA") or admixtures of the latter with other halogenated organic flame retardants. Most preferably TBBA is present in an amount of 50% by weight or more relative to the total halogenated organic flame retardant.

The flame retardant ingredients, when solid, are supplied in pulverulent form, and may be incorporated into the polyolefin by conventional techniques, i.e. in mixers or blenders, but preferably in an extruder. It has been found that preparation of a master batch of the same or different polyolefin or other polyolefin compatible polymer, and containing approximately 2 to 5 times, preferably 2.5 to 4 times the final FR weight percentage is particularly useful. For example, a master batch containing about 30 weight percent organic flame retardant, 32 weight percent alumina trihydrate, and 10% antimony trioxide, balance polypropylene polymer, is highly useful. The master batch is then blended or "diluted" with additional polymer in an extruder prior to injection molding. By "extruder" is meant a screw-type device used to blend thermoplastics to form extrudates or to supply molten thermoplastic to an injection molding machine. The term should not be viewed as limiting, and other mixers may in principle be used.

By the term "polyolefin compatible" or simply "compatible" is meant a polymer which can be blended with polyolefin molding resin and molded into a polyolefin pallet or subassembly thereof while maintaining sufficient strength properties. The compatible polymer may phase separate to form small polymer particles or an interpenetrating polymer network, or may be miscible with the polyolefin. It is preferred that the compatible polymer be itself a polyolefin, particularly the same polyolefin or a polyolefin similar in composition to the polyolefin molding resin. For example, when polypropylene homopolymers or copolymers are used as the polyolefin molding resin, it is preferred that a polypropylene polymer be the polyolefin-compatible polymer of the flame retardant master batch.

The FR package of the present invention may also be used with auxiliary flame agents. Examples include nitrogenous organic compounds such as urea, melamine, and formaldehyde condensates thereof, in the form of powders, prills, fibers, etc., intumescents such as sugars and starches; carbon dioxide generators such as the various metal carbonates, and water generators such as hydrated metal salts. This list is exemplary, and not limiting.

Thus, in preferred embodiments, the pallets of the subject invention are molded of a plurality of subassemblies, which are then joined together, preferably by fusion bonding. In this manner, the composition of the various subassemblies may be varied to optimize pallet physical properties as well as flame retardant properties. For example, one or more of the subassemblies may contain a filler, fibrous reinforcement, or both. Likewise, as indicated previously, those subassemblies which contribute most to flammability may be more highly filled and may also contain higher levels of flame retardant. This is particularly true of the top deck of the pallet. Preferably, all subassemblies contain flame retardant, however.

Preferred pallets have a top deck, a bottom deck, and most preferably a plurality of columns between the top and bottom decks. At least the top deck and preferably all subassemblies are molded from polyolefin resin to which has been added a flame retardant master batch comprising 20 weight percent or more, preferably 20 to 25 weight percent, and most preferably 25 to 35 weight percent of one or more halogenated flame retardant(s); 20 weight percent or more, preferably 20 to 40 weight percent, and more preferably 25 to 40 weight percent alumina trihydrate; and 6 weight percent or more, preferably 6 to 15 weight percent, and more preferably 8 to 12 weight percent of antimony trioxide, at least 10% by weight of the master batch being an olefin compatible polymer.

Having generally described this invention, a further understanding can be obtained by reference to certain specific examples which are provided herein for purposes of illustration only and are not intended to be limiting unless otherwise specified.

EXAMPLE 1 AND COMPARATIVE EXAMPLE C1

Pallets were manufactured by injection molding of subassemblies from polypropylene resin. The subassemblies were assembled into completed pallets and joined together by fusion bonding. The pallet of Example 1 included the FR package of the present invention, added as a master batch containing 30% FR-720 halogenated organic flame retardant, 32% alumina trihydrate, and 10% antimony trioxide, remainder polypropylene. The master batch was added to the extruder with polypropylene resin such that the final polymer of the Example 1 pallet contained 9% FR-720 halogenated organic flame retardant, 9.6% alumina trihydrate, and 3% antimony trioxide. The comparative Example C1 contained no FR package.

Pallet Example
1 C1
Idle Storage Test pass fail
Commodity Storage Test pass fail



EXAMPLE 2 AND COMPARATIVE EXAMPLE C2

An Idle Storage Test as previously described was conducted in stacked 48×40 two-piece construction polymer pallets (polypropylene) which include the FR composition of the subject invention (Example 2). The average steel beam temperatures were plotted against time for these subject invention pallets and standard 48×40 softwood pallets. The results were presented graphically in FIG. 2. The subject invention pallets produced considerably lower temperatures 10 than the wood pallets 11, and pass the Idle Storage Test. Polyolefin pallets containing no FR package exhibit higher temperatures than do the softwood pallets, and do not pass the test. The horizontal line 12 represents the pass/fail limit.

The results indicate that the flame retardant package of the subject invention is suitable for use in pallets, where unique flame retardant properties are required. The subject invention pallet Example 1 was able to pass both Underwriters Laboratory pallet tests, while a similar pallet of the same base molding resin did not. Likewise, the Example 2 pallet shows considerable improvement over wood pallet flammability.

While embodiments of the invention have been illustrated and described, it is not intended that these embodiments illustrate and describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention.

* * * * *
Other References

* "Intumescents: Coating Contains Dual Components," Flame Retardancy News, vol. 11; Issue 7, Jul. 1, 2001.
* Renstrom, R., "Clean Rooms Getting Cleaner," Plastics News, vol. 13, N. 30, Sep. 24, 2001.
* "Prototype Production will Utilize Breakthrough Thermoplastic Flow Forming Technology to Achieve Superior Performance and Economic Results," Las Vegas Business Wire, Jul. 23, 2001.
* English Abstract corresponding to JP 11278485 A.
* Underwriters Laboratories, Inc. "UL 2335 Performance Testing".



We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Additive Masterbatch Functional Concentrates

Say you need an additive to improve your processing conditions. JIEFU can provide slip/antiblock masterbatches, plasticizers or processing aids for film blowing, extrusion and molding. We can also supply you with a material to increase your cycle time, even in multi-cavity tools.

If you are looking to enhance the quality and strength, look and feel of your end product, our Flame retardant masterbatches,antimony trioxide masterbatches,anti-static masterbatches, anti-fogging masterbatches, UV masterbatches, heat stabilizers, FR packages, varying mineral additives, anti-oxidants, chemical couplers, optical brighteners and reflectants are what you want.

All of these additive masterbatches are available in different resin types and with variable active ingredient loadings that can be specially developed for use at a suggested addition rate. At your request, JIEFU can also manufacture tailor-made additives for your particular industry. Simply tell us what properties your finished goods need to exhibit and our technical specialists can do the rest! Choose from the following possibilities:

Functions: Flame retardant, Antioxidants, Slip Agents, Impact Modifiers, Antiwarp Concentrates, Nucleating Agents, Scratch Resistance, Blowing Agents, UV Stabilizers--HALS and UV Screens.

Resins: Polycarbonate, Nylon, Acetal, Polypropylene (Homopolymer, Clarified, Copolymer), ABS (Acrylonitrile, Butadiene, Styrene), SAN, PVC (Rigid, Plasticized), Polyethylene (HDPE, LLDPE, LDPE), Polystyrene (GPPS, MIPS, HIPS), TPE/TPO, Polyurethane


Brand Name Component
FR-M001 Decabromodiphenyl Ethane + Antimony Trioxide = masterbatches
FR-M002 Antimony Trioxide masterbatches EVA80.EAV90;PE80,PE90,PVC85,PP80ETC…
FR-M003 Magnesium hydroxide Masterbatch PE80,90,EVA89,90,PVC80,90…ETC
FR-M004 Decabromodiphenyl Oxide + Antimony Trioxide = masterbatches
FR-M005 Decabromodiphenyl Oxide
Brominated Polystyrene



We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Anti-bacterial masterbatches

Main Usage
·plastic-injection ·plastic-blown ·casting
·plastic-extrusion ·film-blowing · foaming

Main Final Products
·household electronics ·toy ·packing Material
·Synthetic Fibre ·household utensils ·vehicles
·hygiene equipment ·sport articles

Product Characteristics
These series color masterbatches are of several advanced properties as anti-bacterial effectively, no harm to persons, no pollution, good dispersing quality, high heat resistance, brightness resistance, etc.
They seldom effect the physics capability of products.

Application Ratio and Method
Mix this series Masterbatches with the stuff resin at ratio of 1:20 to 1:50 (different ratio decided by the user requirement or products property). After simply stirring the mixture to homogeneous (no addictive agent needed),we can get the final color products as we want.

Main Technical Index
Appearance [ Granule form, equal in size and shad ]
Heat resistance (0C) [ 250 ]
Anti-bacterial rate [ 3% input will effectively kill 88% ~100% Escherichia coli，staphylococcus aureuspseudomonad, etc. (4 hours after)]
Water ratio(%) [ ≤0.3 ]


We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Transparent Filler Masterbatch

I. Main Application Transparent Filler Masterbatch is a kind of advanced modified Filler MB made of inorganic transparent powder material and other special additives. Its refraction is similar to polyolefin plastics. When the application ratio is around 5-10%, the transparency of HDPE film is distinctly improved. And it will not affect the transparency of LDPE film. It is used for first and mid grade polyolefin material in the process of extrusion, injection, plastic blowing, film blowing, casting, wire drawing, etc. When it is put into use, we can reduce material cost, and improve the character of final products.

II. Technique Index
1. Granule size for inorganic transparent powder: ≤10μm
2. Whiteness : ≥98%
3. Application ratio: Mix transparent filler MB with the stuff resin from the ratio of 8% to over than 15% (different ratio decided by the product and user).

III. Product Characteristics
Compare to normal filler MB, transparent filler MB is with below superiority:
1. With small gravity, it will remain parts of the physical and mechanical property of plastic products.
2. Transparent Filler MB is with good dispersing quality to assure the smooth appearance of plastic products, so that it can guarantee good printing quality of surface for first and mid grade plastic products.
3. Transparent filler MB is with good heating seal property and certain anti-adhesive property.
4. Since the transparent powder material is introduced, under same application ratio to normal filler MB, the effect on transparency of material is distinctly reduced.

IV. Remarks
Stored in ventilated, dry and cool place. Transparent Filler MB is easily to absorb moisture from the air. So please use out soon after opening the package.


We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more

[+/-] : Calcium Carbonate masterbatches

I. Main Application
Filler Masterbatch is made of high quality Calcium Carbonate
and other special additives after extrusion molding from high performance twin-screw machine. It is widely used for polyolefin material in the process of extrusion, injection,
plastic blowing, film blowing, casting, etc. When it is put into use, we can reduce material cost, and improve the character of final products.

II. Technique Index
1. Granule size for Calcium Carbonate: ≤10μm
2. Whiteness : ≥98%
3. Application ratio: Mix Filler MB with the stuff resin from the ratio of 10% to more than 30% (different ratio decided by the product and user).

III. Product Characteristics
1. Improve the anti-heating, rigidity and tightness property.
2. Remove the surface light from plastic products, to get sub-light effect.
3. Improve the surface antifriction and antislip property of plastic products.
4. Reduce shrinkage ratio of final products to improve size stability.
5. Reduce fire heating quantity of plastic products to reduce second pollution.
6. Improve surface printing property of plastic to reduce needed electric current under surface corona process.
7. Provide breathe free to film products.
8. Improve heat-conduction property of plastic material to reduce molding period.
9. Reduce the application ratio of white color masterbatch.

IV. Remarks
Stored in ventilated, dry and cool place. Filler MB is easily to absorb moisture from the air. So please use out soon after opening the package.



We can supply any quantity and any kind of Antimony products from stock.would you please inform us how many you need and your target price, then we will confirm ASAP. We are sincerely hope to do business with you and establish long term business relationship with your respectable company.

Look forward to hearing from you soon.

Best regards,

Sam Xu
Contact me:
MSN: xubiao_1996@hotmail.com
GMAIL: samjiefu@gmail.com
SKPYE:jiefu1996


Chinese antimony market

...
read more